HIGH SPEED STEEL Performance FOR HSS-W18
HSS CODE: W18Cr4V (W18)
Chemical compositons(%): C Si Mn W Mo Cr V Co 0.70-0.80 0.15-0.65 0.10-0.40 17.50-19.00 <0.3 3.80-4.40 1.00-1.40
International Code:
ASTM: T1
UNS: T12001
JIS:SKH2
DIN:
BS: BT1
NF: HS18-0-1
ROCT: P18
ISO: HS18-0-1
China:W18
Density Annealed(g/cm):8.7
Heat treatment:Starting: 1100 Finishing:900
Usage:For making cutters of High speed Tool Bits,Drill Bits,Endmills,Reamers etc.And Taps,Dies,Rolling dies,Saw bladed etc.
Anneal temperature (℃) 840-860
Stress relief Temperature(℃):600-650
Quench temperature (℃):1270-1285
Coolant media of quench : salt bath at 600℃,or Oil cool or air cool
Normal temperature of temper(℃): 550-570
Quench and temper HRC: 63-66
Bending Strength(Mpa):
Impact Toughness(MJ/㎡):
HRC at 600℃(HRC):
Character:representative Steel Grade of W -Mo series,with High Hardness,High Hardness in high temperature.High Red Hardness.The wide range of Heat treatment temperature.Not easy over heating when Quenching. good grindability,not easy to oxidize and decarburized.But hot forming inferior than Mo-series of HSS.