HIGH SPEED STEEL Performance FOR HSS-W4
HSS CODE: W4Mo3Cr4VSi (W4)
Chemical compositons(%):
C Si Mn W Mo Cr V 0.88-0.98 0.20-0.40 0.20-0.40 3.50-4.5 2.5-3.5 3.80-4.40 1.20-1.80
International Code:
ASTM:
UNS:
JIS:
DIN:
BS:
NF:
ROCT:
ISO:
China:W4
Density Annealed(g/cm):7.95
Heat treatment:Starting: 1100 Finishing:900
Usage: Mainly for Twist Drill bits,Jig Saw Blade. Also for other tools of low performance.Sometime for high loading mould, high temperature bearing and speical heat-resistance and wear resistant parts in areo.
Anneal temperature (℃) 840-860
Stress relief Temperature(℃):600-650
Quench temperature (℃):1170-1190
Coolant media of quench : salt bath at 600℃,or Oil cool or air cool
Normal temperature of temper(℃): 540-560
Quench and temper HRC: 63-66
Bending Strength(Mpa):
Impact Toughness(MJ/㎡):
HRC at 600℃(HRC):
Character:High performance of low Alloy HSS. With related HRC,Red Hardness and strengthen.Good Hot reforming.Good Grindability.