HIGH SPEED STEEL Performance FOR HSS cobalt 8%-M42
HSS CODE: W6Mo5Cr4V2Co8 (M42)
Chemical compositons(%): C Si Mn W Mo Cr V Co
1.05-1.15 0.25-0.45 0.15-0.40 1.15-1.85 9.00-10.0 3.50-4.25 0.95-1.35 7.75-8.75
International Code:
ASTM: M42
UNS: T11342
JIS:SKH59
DIN: S2-10-1-8
BS: BM42
NF: HS2-9-1-8
ROCT: P6M5K5
ISO: HS2-9-1-8
China:M42
Density Annealed(g/cm):7.95
Heat treatment:Starting: 1100 Finishing:900
Usage:For making all kinds complex and high precison cutters e.g.precision Broching, Endmills,special tool Bits and various high HRC cutters.Usually used for some difficult working,Supper-high tensile materials cutting.
Anneal temperature (℃) 840-860
Stress relief Temperature(℃):600-650
Quench temperature (℃):1160-1190
Coolant media of quench : salt bath at 600℃,or Oil cool or air cool
Normal temperature of temper(℃): 530-560
Quench and temper HRC: 66-68
Bending Strength(Mpa): 2650-3730
Impact Toughness(MJ/㎡): 0.23-0.29
HRC at 600℃(HRC): 55.2
Character:It's a super Hardness of High Carbon with Co of W-Mo series. With High Hardness at Normal and High temperature.High Red Hardness and good grandability. Especially there are good performance in cutting and grinding hard-working steel(super High pressure resistance steel).But Pressure resistance not very good.