ITEM:
HSS CODE: W9Mo3Cr4V (W9)
Chemical compositons(%):
C Si Mn W Mo Cr V Others
0.77-0.87 0.20-0.40 0.20-0.40 8.50-9.50 2.70-3.30 3.80-4.40 1.30-1.70
International Code:
ROCT: P9M3
China:W9
Density: Annealed(g/cm) 8.23
Heat treatment:
Starting: 1100 Finishing:900
Usage:It’s a subsidiary of W18 Cr4 and W6Mo5Cr4V2.Suitable for making all kinds of tools.
Anneal temperature (℃) 840-860
Stress relief Temperature(℃):600-650
Quench temperature (℃):1210-1230
Coolant media of quench : salt bath at 600℃,or Oil cool or air cool
Normal temperature of temper(℃): 540-560
Quench and temper HRC: 63-66
Bending Strength(Mpa): 4000-4500
Impact Toughness(MJ/㎡): 0.35-0.40
HRC at 600℃(HRC):
Character: Its a newly developed general used HSS of W-Mo series.
The performance equal to W18Cr4V(T1) and W6Mo5Cr4V2(M2) Good Grandability and Good hot reforming.Easy to forge and Roll.But its comprehensive use property superior than T1 and HSS-M2.